| 物理性能 |
额定值
|
单位制
|
测试方法
|
| 密度 |
2.11
|
g/cm³
|
ASTM D1505 |
| 薄膜 |
额定值
|
单位制
|
测试方法
|
| 割线模量 | ASTM D882 | ||
|
MD: 100 µm
|
1240
|
MPa
|
|
|
TD: 100 µm
|
1240
|
MPa
|
|
| 抗张强度 | ASTM D882 | ||
|
MD: 屈服, 100 µm
|
51.7
|
MPa
|
|
|
TD: 屈服, 100 µm
|
37.9
|
MPa
|
|
| 伸长率 | ASTM D882 | ||
|
MD: 屈服, 100 µm
|
190
|
%
|
|
|
TD: 屈服, 100 µm
|
200
|
%
|
|
| 水气透过率 | ASTM F1249 | ||
|
40°C, 100 µm, 75% RH
|
0.048
|
g·mm/m²/atm/24 hr
|
|
|
38°C, 100 µm, 100% RH
|
0.0042
|
g·mm/m²/atm/24 hr
|
|
|
25°C, 100 µm, 60% RH
|
0.0093
|
g·mm/m²/atm/24 hr
|
|
|
30°C, 100 µm, 60% RH
|
0.016
|
g·mm/m²/atm/24 hr
|
| 热性能 |
额定值
|
单位制
|
测试方法
|
| 结晶峰温 (DSC) |
211
|
°C
|
ASTM D3418 |