| 物理性能 |
额定值
|
单位制
|
测试方法
|
| 密度 |
2.11
|
g/cm³
|
ASTM D1505 |
| 薄膜 |
额定值
|
单位制
|
测试方法
|
| 割线模量 | ASTM D882 | ||
|
MD: 20 µm
|
1400
|
MPa
|
|
|
TD: 20 µm
|
1340
|
MPa
|
|
| 抗张强度 | ASTM D882 | ||
|
MD: 屈服, 20 µm
|
89.6
|
MPa
|
|
|
TD: 屈服, 20 µm
|
47.9
|
MPa
|
|
| 伸长率 | ASTM D882 | ||
|
MD: 屈服, 20 µm
|
120
|
%
|
|
|
TD: 屈服, 20 µm
|
250
|
%
|
|
| 水气透过率 | ASTM F1249 | ||
|
40°C, 20 µm, 75% RH
|
0.26
|
g·mm/m²/atm/24 hr
|
|
|
38°C, 20 µm, 100% RH
|
0.29
|
g·mm/m²/atm/24 hr
|
|
|
25°C, 20 µm, 60% RH
|
0.039
|
g·mm/m²/atm/24 hr
|
|
|
30°C, 20 µm, 60% RH
|
0.062
|
g·mm/m²/atm/24 hr
|
| 热性能 |
额定值
|
单位制
|
测试方法
|
| 结晶峰温 (DSC) |
211
|
°C
|
ASTM D3418 |